DESCRIPTION

TamPur 130 / TamKat 130 is a single-shot hydrophobic polyurethane based on MDI in combination with polyether polyols and an amine based catalyst. The system only reacts when it comes into contact with water, producing a semi-flexible polyurethane foam.

KEY BENEFITS

  • Potable water certified
  • Can withstand high hydrostatic pressures
  • Variable reaction times
  • Semi-flexible
  • Reacts with saline and mineral water
  • Medium viscosity
  • Solvent-free, environmentally safe.
TYPICAL APPLICATIONS
  • Sealing against water ingress
  • Sealing against leaking cracks and joints
  • Sealing against water in masonry and brickwork
  • Void filling
  • Back grouting
TECHNICAL DATA

TamPur 130

Appearance

Brown liquid

Viscosity at 25oC
Brookfield DV 11 spindle no.2
at 60 rpm

350 – 450mpa.s

Flash point

> 180oC

Density at 25oC

1.16

TamKat 130

Appearance

Clear liquid

Viscosity at 25oC
Brookfield DV 11 spindle no.2 at 60 rpm

30 -40m Pa.s

Flash point
density at 25oC
>130oC
1.03

Testing TamPur 130 – All tests carried out using the following mix ratio.

  • TamPur 130: 100 parts by weight
  • TamKat 130: As a percentage of Tampur 130 by weight , as stated in the results.
  • Water: In all the tests,10 parts by weight.
Cream Time

TamKat

1%

2%

5%

10%

15oC

33sec

33sec

30sec

26sec

25oC

30sec

30sec

26sec

24sec


Rise Time

TamKat

1%

2%

5%

10%

15oC

12min;
50sec
11m;
5sec
6m;
20sec
3m;
10sec

25oC

12min;10 sec

10min;10 sec

4min;30 sec

3m


Foaming Ratio

TamKat

1%

2%

5%

10%

15oC

>4X

>9X

>14X

>20X

25oC

>6X

>15X

>20X

>30X


All technical data stated herein based on tests carried out under laboratry conditions.

APPLICATION GUIDELINES

TamPur 130 / TamKat 130 is a complete system for void filling and leak sealing in concrete or masonry structures and sandy soils.

Adaptable reaction time is possible by varying the catalyst ratio from between 2% to 10%.

Reaction with water results in the formation of a semi-flexible polyurethane foam which is hydrophobic and chemically resistant. The reaction time can be set from 3 to 14 minutes. (See table of reaction times overleaf.) The pre- mixed resin can be pumped by means of a single component injection pump that is equipped for high pressure. Following the injection, the pump must be thoroughly cleaned with TamPur Cleaner.

Note: Always make sure that the material is homogeneous, mix the resin using a dry clean drill and paddle mixer for a minimum of 15 sec before application.

It is recommended that the material be conditioned to appropriate temperatures for at least 12 hours prior to application.

Important: Keep containers sealed whilst not being used. Moisture may be absorbed into the TamPur from the atmosphere causing it to react. Careful consideration should be given to applications below 10°C on a falling thermometer to avoid possible crystallisation.

STORAGE

TamPur 130 should be stored at room temperature (min 10°C and max 38°C), kept dry and out of direct sunlight. If these conditions are maintained and the product packaging is unopened, then a shelf life of 1 year can be expected.

HEALTH & SAFETY

TamPur 130 should only be used as directed. We always recommend that the Safety data sheet is carefully read prior to application of the material. Our recommendations for protective equipment should be strictly adhered to for your personal protection. The Safety data sheet is available upon request from your local Normet representative.